Analisa Kekerasan Baja Carbon Steel 1045 Akibat Perlakuan Panas Yang Di Dinginkan DenganUdara,Air dan Oli Menggunakan Metode Vickers

Rizky Auditya Putra

  • Rizky Auditya Putra Universitas harapan medan
  • Junaidi Junaidi Universitas Harapan Medan
  • Fadly A Kurniawan Universitas Harapan Medan
Keywords: steel, carbon steel, properties of carbon steel, hardness test, before and after heat treatment with water, oil, air as a coolant

Abstract

ABSTRACT

Steel is a material that we often use to make tools, both heavy and light equipment as well as food containers and many others. Steel is the material most widely used as an industrial material, because steel has various physical and mechanical properties. Carbon steel is an alloy between iron and carbon with small amounts of Si, Mn, P, S, and Cu. The nature of carbon steel is very dependent on the carbon content, if the carbon content increases, the strength and hardness will also increase. The property of steel which can undergo great deformation under the influence of high tensile stress without breaking or breaking is called the ductility property. The method used in this research is descriptive method, which is a method used to carefully test an object being studied so that accurate data will be obtained after data collection is complete, data processing will be carried out using a predetermined formula. Average value - diagonal average identification before heat treatment with a pressure load of 2000 grams at point 1 (top) 111.85 at point 2 (middle) 107.4 and at point 3 (bottom) 118.9. Number of hardness of the vickers with a load of 2000 grams at point 1 (top) 296.5 at point 2 (middle) 321.6 and at point 3 (bottom) 262.4. The average number of 1045 carbon steel testing before heat treatment is 293.5. From the conclusion of the study using 1045 carbon steel steel, there can be differences in the average diagonal identification value after heat treatment using water as a coolant with a pressure of 2000 grams at point 1 (above) 71 at point 2 (center) 131.80 and at point 3 ( bottom) 93. The number of vickers hardness with a load of 2000 grams at point 1 (top) 735.8 at point 2 (middle) 213.5 and at point 3 (bottom) 428.8 The average number of testing 1045 carbon steel after heat treatment with water as a coolant is 459.37. The diagonal mean value of identification after heat treatment using oil media as a coolant with a pressure load of 2000 grams at point 1 (above) 96.81 at point 2 (center) 107.54 and at point 3 (bottom) 100.09. Vickers hardness figure with a load of 2000 grams at point 1 (top) 395.7 at point 2 (center) 320.7 at point 3 (bottom) 370.2. The average number of testing 1045 carbon steel after heat treatment using oil media as a coolant with a value of 362.20. The diagonal mean value of identification after heat treatment using air as a coolant with a pressure load of 2000 grams at point 1 (top) 132.51 at point 2 (center) 140.38 and at point 3 (bottom) 125.49. Vickers hardness figure with a load of 2000 grams at point 1 (top) 211.2 at point 2 (center) 188.2 at point 3 (bottom) 235.5. The average number of testing 1045 carbon steel after heat treatment using air as a coolant with a value of 211.63.

Keywords: steel, carbon steel, properties of carbon steel, hardness test, before and after heat treatment with water, oil, air as a coolant

 

Downloads

Download data is not yet available.

Author Biographies

Junaidi Junaidi, Universitas Harapan Medan

Program Studi Teknik Mesin

Fadly A Kurniawan, Universitas Harapan Medan

Program Studi Teknik Mesin

References

[1] William F., “Foundations of materials science and engineering McGraw-Hill series in materials science,” p. 111661, 2006.
[2] “pengertian unsur jenis dan pembentukan baja.” kajianpustaka.com (accessed Aug. 11, 2020).
[3] S. Surdia, Tata dan Saito, “Pendahuluan Buku Ajar,” Pengetah. Bahan Tek. PT. Pradnya Paramita. Jakarta .
[4] “M at e r i a l s t e c h n o l o g y 2.”
[5] Kadir, Statistika Terapan Kosep, Contoh dan Analisis Data dengan Program SPSS/Lisrel dalam Penelitian. 2015.
[6] S. Djaprie, E. George, S. Djaprie, and E. George, “Metalurgi fisik modern dan rekayasa material / R . E . Smallman , R . J Bishop ; penterjemah Sriati Djaprie Teknologi mekanik / oleh B . H . Amstead , Phillip F . Ostwald , Myron L . Van Vlack ; alih bahasa Sriati Djaprie , M . E ., M . Met . Metalurgi fisik modern & rekayasa material / oleh R . E . Smallman dan R . J . Bishop ; penerjemah Sriati Djaprie Ilmu dan teknologi bahan ( ilmu logam dan bukan logam ) / oleh Lawrence H . Van Vlack ; diterjemahkan oleh Sriati Djaprie Ilmu dan teknologi bahan : ilmu logam dan bukan logam / Lawrence H . Van Vlack ; alih bahas Sriati Djaprie Teknologi mekanik jilid 1 / oleh : B . H . Amstead , Phillip F . Ostwald , Myron L . Begeman ; alih bahasa : Sriati Djaprie,” pp. 9–10, 1999.
[7] “Page 1,” p. 1989, 1989.
[8] T. Akhir, A. Rizky, J. Teknik, and M. Universita, “Tugas Akhir Pendahuluan,” pp. 1–4.
Published
2020-10-30
How to Cite
[1]
R. Putra, J. Junaidi, and F. Kurniawan, “Analisa Kekerasan Baja Carbon Steel 1045 Akibat Perlakuan Panas Yang Di Dinginkan DenganUdara,Air dan Oli Menggunakan Metode Vickers”, Jurnal Simetri Rekayasa, vol. 2, no. 2, pp. 86-91, Oct. 2020.

Most read articles by the same author(s)

1 2 > >>