ANALISA PERUBAHAN SIFAT MEKANIS BAJA AISI 1045 BERDIAMETER 25 MM AKIBAT PERLAKUAN PANAS TEMPERING DAN MENGGUNAKAN TENSILE TEST DENGAN MEDIA PENDINGIN AIR

  • Rifki Gunawan Teknik Mesin
  • Junaidi Junaidi Universitas Harapan Medan
  • Fadly A. Kurniawan Universitas Harapan Medan
DOI: https://doi.org/10.35447/jitekh.v8i1.296
Keywords: AISI 1045 steel, Heat treatment, Tensile test (tensile test)

Abstract

In the process of work experienced, especially the process of selling heat received during the processing. If the cooling process is carried out slowly, it will be possible to reach each type of micro balanced according to the chemical composition and temperature of the steel. In the manufacturing process, the required chemical composition is obtained when steel is in a liquid phase at high temperatures. During the cooling process of the melting temperature, steel begins to turn into a solid phase at a temperature of 13,500 C, in this phase there is a change in micro-structure. Normalization is the process of heating the metal until it reaches the austenite phase which is then desired slowly in AC media. The cooling results are perlite and ferrite but the results are much smoother than annelling. The voltage results after the tempering process showed the highest value at 200 oC is 1482, 311 N / mm2 and the lowest value at 400 oC was 1104, 75 N / mm2.

Downloads

Download data is not yet available.

References

[1] I. Rahardi, “PENGARUH PENGGUNAAN STRUKTUR BAJA PADA BANGUNAN 2 TINGKAT,” IMAJI, vol. 9, no. 6, 2020.
[2] S. Kirono, E. Diniardi, and I. Prasetyo, “Aalisa Perubahan Dimensi Baja AISI 1045 Setelah Proses Perlakuan PANAS ( Heat Treathment ),” SINTEK J. J. Ilm. Tek. Mesin, pp. 1–11, 2010.
[3] N. Nukman, “Sifat mekanik baja karbon rendah akibat variasi bentuk kampuh las dan mendapat perlakuan panas,” J. REKAYASA MESIN, vol. 9, no. 2, pp. 37–43, 2009.
[4] Y. Rizal, “Analisa Pengaruh Media Quench Terhadap Kekuatan Tarik Baja Aisi 1045,” J. APTEK, vol. 6, no. 02, pp. 183–190, 2014.
[5] S. Subagiyo, S. Hadi, L. Agustriana, and K. Kasiyanto, “Analisis Kekuatan Tarik dan Kekerasan Baja Tahan Karat Martensitik Fasa Ganda Hasil Perlakuan Panas dengan Variasi Temperatur dan Media Pendingin,” J. Ilm. Teknol. FST Undana, vol. 11, no. 2, pp. 18–23, 2018.
[6] R. Rifnaldi, “Pengaruh Perlakuan Panas Hardening Dan Tempering Terhadap Kekerasan ( Hardness ) Baja Aisi 1045,” pp. 950–959, 2019.
[7] Hamdani, “Pengaruh Masukan Panas Proses Pengelasan Terhadap Sifat Mekanik Baja Aisi 1045 : Suatu Kajian Eksperimental,” Polimesin, vol. 1, no. 2, pp. 1–8, 2019.
[8] R. B. S. Majanasastra, “Karbon Tinggi ( Aisi D2 ) Hasil Perlakuan Panas,” vol. 1, no. 2, pp. 61–66, 2013.
Published
2020-03-30
How to Cite
Gunawan, R., Junaidi, J., & Kurniawan, F. A. (2020, March 30). ANALISA PERUBAHAN SIFAT MEKANIS BAJA AISI 1045 BERDIAMETER 25 MM AKIBAT PERLAKUAN PANAS TEMPERING DAN MENGGUNAKAN TENSILE TEST DENGAN MEDIA PENDINGIN AIR. JiTEKH, 8(1), 6-10. https://doi.org/https://doi.org/10.35447/jitekh.v8i1.296